Homemade soldering flux

Written by janet lee-amies
  • Share
  • Tweet
  • Share
  • Pin
  • Email
Homemade soldering flux
When making a pendant, you'll need to solder a bezel onto the metal base. (Hemera Technologies/PhotoObjects.net/Getty Images)

When joining metals together in jewellery-making, there are three important elements: solder, flux and heat. When metal is heated, solder, which is also made of metal, melts to join the pieces together. But during this process metal is also exposed to oxygen, which cause the metal to oxidise or tarnish, and tarnish can prevent solder from melting. Flux works as a catalyst in this process. It helps inhibit oxidisation and enables solder to melt. Flux is commercially available in jewellery supply stores, but you can make your own at home.

Skill level:

Things you need

  • 4 fluid oz. borax
  • 4 fluid oz. trisodium phosphate (TSP)
  • 6 fluid oz. boric acid
  • Pot
  • Wooden spoon
  • Glass jar with lid or plastic bottle with lid

Show MoreHide


  1. 1

    Put about 2 cups of water in the pot. Add the trisodium phosphate, boric acid and borax. Mix using the wooden spoon.

  2. 2

    Place the pot on the stove. Turn heat on high. When the mixture boils, turn the heat down to low. Let the mixture simmer for three to five minutes.

  3. 3

    Turn off heat. Let mixture cool. Pour the liquid flux into a glass jar or plastic bottle. Close the lid tightly until you are ready to use the flux.

Tips and warnings

  • Vary the quantities of ingredients to make more or less flux. The ratio should be 2:2:3 of borax/trisodium phosphate/boric acid.
  • You do not need to be precise with the water, but the flux should be liquid enough to pour easily.
  • Use a pot that you will not be using for food preparation purposes.

Don't Miss

  • All types
  • Articles
  • Slideshows
  • Videos
  • Most relevant
  • Most popular
  • Most recent

No articles available

No slideshows available

No videos available

By using the eHow.co.uk site, you consent to the use of cookies. For more information, please see our Cookie policy.